WD-SJ8016 Sintering flux for submerged arc welding
WD-SJ8016 Sintering flux for submerged arc welding

WD-SJ8016 Sintering flux for submerged arc welding

WD-SJ8016 is an aluminum-alkali type sintered solder with an alkalinity of about 2.6. It has the appearance of 10-60 mesh (2.0-0.28mm) light yellow round particles with small loose packing density

Subclassification：

· Hard Surfacing

电话

Enquiry hotline：

13898363063

Contact us
  • Product description
    • Commodity name: WD-SJ8016 Sintering flux for submerged arc welding
    • Commodity ID: 1057227826437906432

    WD-SJ8016 is an aluminum-alkali type sintered solder with an alkalinity of about 2.6. It has the appearance of 10-60 mesh (2.0-0.28mm) light yellow round particles with small loose packing density

    Standards：

    GB/T17854　　F410-H1Cr13/F308-H0Cr21Ni10

     

    Introduction：

    WD-SJ8016 is an aluminum-alkali type sintered solder with an alkalinity of about 2.6. It has the appearance of 10-60 mesh (2.0-0.28mm) light yellow round particles with small loose packing density, suitable for small welding current, The current is supplied by a DC power source with the wire connected to the positive terminal. Welding process performance is good, easy deslagging, beautiful forming, overlay metal has excellent resistance to intergranular corrosion performance and anti-brittle performance. The flux of the deposited metal is 13Cr system and Cr21Ni10 system, with the Cr13 series solid core wire, flux cored wire, H0Cr21N10 wire, etc., widely used in alloy steel, high alloy steel and stainless steel automatic welding and hard surface overlay welding, especially suitable for hard surface roller repair overlay welding of easy to wear parts.

     

    Applications：
    It can be used for surfacing all kinds of hard surface rolls, such as surfacing continuous casting rolls, rolling mill rolls and feeding rolls.

     

    Flux chemical composition reference value(%)：

    SiO2+TiO2

    CaO+MgO

    Al203+MnO

    CaF2

    S

    P

    15

    35

    20

    25

    ≤0.06

    ≤0.08

     

    Reference value of molten metal composition(%)：

    Welding wire

    C

    Cr

    Si

    Ni

    Mn

    Mo

    S

    P

    H1Cr13

    0.12

    12.65

    0.48

    -

    -

    -

    0.002

    0.025

     

    Hardness reference value：

    Matching wire

    Hardness (HRC)

    Cr13 series flux cored wire

    46-50

     

    Notice：

    1. The flux shall be baked at 300-350°C for 2 hours before use.

    2. Rust, oil, water and other impurities should be removed from the welded parts before welding.

    3. Preheat 300-400℃ before welding.
     

    Key words:
    • Surfacing
    • Welding wire
    • flux