WD-SJ38 Sintering flux for submerged arc welding
Subclassification：
· High Strength Steel
Enquiry hotline：
- Product description
-
- Commodity name: WD-SJ38 Sintering flux for submerged arc welding
- Commodity ID: 20230112005
WD-SJ38 is an aluminum-titanium type sintered flux with alkalinity of 0.7 and appearance of gray-black spherical particles of 10-60 mesh (2.0-0.28mm).
Standard：
GB/T5293 S 43A 0 AR-SU21 AWS A5.17 F7A2-EM12K
Introduction：
WD-SJ38 is an aluminum-titanium type sintered flux with alkalinity of 0.7 and appearance of gray-black spherical particles of 10-60 mesh (2.0-0.28mm). The flux is suitable for high speed welding and fillet welding of thin plate of container type in humid climate area, which has the characteristics of fast welding speed, strong resistance to porosity, easy slag removal for fillet welding and beautiful weld seam formation. It can be used in both AC and DC, and the welding wire is connected to the positive pole when DC is used.
Applications：
It can be used to weld low carbon steel type thin plate containers, street light lamp posts, etc.
Flux chemical composition reference value(%)：
SiO2+TiO2
CaO+MgO
Al203+MnO
CaF2
S
P
30.0
10.0
50.0
5.0
≤0.06
≤0.08
Reference values for mechanical properties of molten metal：
Mating wire Yield strength
(MPa)Tensile strength
(MPa)Elongation
(%)KV2 (J)
0℃
EM12
≥400
480-650
≥22
≥27
Notice：
1. The flux shall be baked at 300-350°C for 2 hours before use.
2. Rust, oil, water and other impurities should be removed from the welded parts before welding.
Key words:- welding
- flux