WD-SJ105 Sintering flux for submerged arc welding


WD-SJ105 is a fluoro-alkali type sintering flux with an alkalinity of about 3.2. It has the appearance of gray-black spherical particles of 10-60 mesh (2.0-0.28mm).

Subclassification:

· High Strength Steel


电话

Enquiry hotline:

Contact us
  • Product description
    • Commodity name: WD-SJ105 Sintering flux for submerged arc welding
    • Commodity ID: 1057227622745726976

    WD-SJ105 is a fluoro-alkali type sintering flux with an alkalinity of about 3.2. It has the appearance of gray-black spherical particles of 10-60 mesh (2.0-0.28mm).

    Standard:

    GB/T5293  S 49 A 4 FB-SU08A  AWS A5.23M-97  F7A4-EHL8  14174-S A FB 1

     

    Introduction:

    WD-SJ105 is a fluoro-alkali type sintering flux with an alkalinity of about 3.2. It has the appearance of gray-black spherical particles of 10-60 mesh (2.0-0.28mm). The flux has advantages as follows: has good moisture absorption resistance; high particle strength; small loose packing density; low flux consumption during welding. The maximum welding current of the flux in the welding process up to 1200A and has arc stability; the formation of short slag after welding; narrow gap de-slagging is easy; do not drip slag in welding small diameter cylinders; beautiful weld formation; pure deposited metal; low SiO2 content, reducing the transition of silicon; has a high low temperature impact toughness. The wire is connected to the positive electrode when DC welding. With the corresponding wire, multi-layer welding, double-sided single-pass welding, multi-wire welding and narrow gap submerged arc welding, etc., can be used to weld higher strength marine steel, pressure vessel steel, pipeline steel, marine platforms and fine grain structural steel for important welded products.

     

    Applications:

    It can be used for butt and fillet welds of ships, pressure vessels, storage tanks, steel structures, bridges, spiral welded pipes and other structures.

     

    Flux chemical composition reference value(%):

    SiO2+TiO2

    CaO+MgO

    Al203+MnO

    CaF2

    S

    P

    9.5

    33.5

    20.4

    36.6

    0.024

    0.028

     

    Reference values for mechanical properties of molten metal:

    Mating wire

    Yield strength
    (MPa)

    Tensile strength
    (MPa)

    Elongation
    (%)

    KV2 (J)

    -20°C

    -40°C

    H08A

    420

    520

    33

    80

    60

    H10Mn2

    450

    560

    30

    85

    65

     

    Notice:

    1. The flux shall be baked at 300-350°C for 2 hours before use.

    2. Rust, oil, water and other impurities should be removed from the welded parts before welding.
     

    Key words:
    • wd-sj105
    • welding
    • flux
    • Pressure vessel
    • Welding wire