WD-H08MnA/WD-EM12 Submerged arc welding wire
WD-H08MnA/WD-EM12 Submerged arc welding wire

WD-H08MnA/WD-EM12 Submerged arc welding wire

Medium manganese and low silicon type wire, matched with medium manganese and silicon flux, insensitive to rust on base material, excellent weld channel formation and slag removal performance.

Subclassification：

· Submerged Arc Welding Wire

电话

Enquiry hotline：

13898363063

Contact us
  • Product description
    • Commodity name: WD-H08MnA/WD-EM12 Submerged arc welding wire
    • Commodity ID: 20230112002

    Medium manganese and low silicon type wire, matched with medium manganese and silicon flux, insensitive to rust on base material, excellent weld channel formation and slag removal performance.

    Standards：

    GB/T5293　　SU26　　AWS　　EM12

     

    Introduction：
    Medium manganese and low silicon type wire, matched with medium manganese and silicon flux, insensitive to rust on base material, excellent weld channel formation and slag removal performance. Single wire, double wire, AC and DC welding are available.

     

    Applications：
    Suitable for multi-layer welding of medium and thick plates of general structures.

     

    Reference value of chemical composition of welding wire and deposited metal (%)：

     

    C

    Mn

    Si

    S

    P

    Cu

    Chemical composition of welding wire

    ≤0.10

    0.80-1.10

    ≤0.07

    ≤0.03

    ≤0.03

    ≤0.20

    Molten gold chemical composition

    0.06

    1.16

    0.21

    0.01

    0.02

    0.02

     

    Reference values for mechanical properties of molten metal：

    Yield strength
    (MPa)

    Tensile strength
    (MPa)

    Elongation
    (%)

    KV2 (J)

    -30°C

    465

    555

    30

    40

     

     

    Key words:
    • welding
    • Welding wire
    • Metal