WD-SJ102 Sintering flux for submerged arc welding
WD-SJ102 Sintering flux for submerged arc welding

monaco WD-SJ102 Sintering flux for submerged arc welding

WD-SJ102 is a fluoro-alkali type sintering flux with an alkalinity of about 3.4, with the appearance of gray spherical particles of 10-60 mesh (2.0-0.28mm).

Category:

monaco· Low Alloy Steel

Phone:400-888-8888

Inquire

Product Description

Standards：

GB/T5293　　S49A4FB-SU34　　GB/T36034　　S62A4FB-SU31　　AWS A5.17　　F7A4-EH14　　141 74-SAFB1

 

Introduction：
WD-SJ102 is a fluoro-alkali type sintering flux with an alkalinity of about 3.4, with the appearance of gray spherical particles of 10-60 mesh (2.0-0.28mm). The flux in the welding process shows advantages as follows: arc stability; easy deslagging; beautiful weld seam formation; pure deposited metal; has a high low-temperature impact toughness. Welding can be used in both AC and DC, DC welding wire connected to the positive electrode.

 

Applications：
With the appropriate welding wire (such as H08MnA, H10Mn2, H08MnMoA) can weld a variety of low-alloy structural steel, higher strength hull structural steel, pressure vessel steel. It can be used for multi-pass welding, double-sided single-pass welding, multi-wire welding and narrow gap submerged arc welding.

 

Flux chemical composition reference value(%)：

SiO2+TiO2

CaO+MgO

Al203+MnO

CaF2

S

P

15.4

42.4

19.6

22.5

0.028

0.030

 

Reference values for mechanical properties of molten metal：

Mating wire

Yield strength
(MPa)

Tensile strength
(MPa)

Elongation
(%)

KV2 (J)

-20°C

-40°C

H10Mn2

450

550

30

-

125

H08MnMoA

575

680

22

-

65

H08Mn2MoA

665

780

21

-

50

 

Notice：

1. The flux shall be baked at 300-350°C for 2 hours before use.

2. Rust, oil, water and other impurities should be removed from the welded parts before welding.
 