WD-SJ612 Sintering flux for submerged arc welding
WD-SJ612 Sintering flux for submerged arc welding

Papua New Guinea WD-SJ612 Sintering flux for submerged arc welding

WD-SJ612 flux is a calcium silica type sintered flux with an alkalinity of about 1.0.

Category:

Papua New Guinea· Hard Surfacing

Phone:400-888-8888

Inquire

Product Description

Standards：

GB/T17854　　F309-H0Cr24Ni13　　F308L-H00Cr24Ni13

 

Introduction：

WD-SJ612 flux is a calcium silica type sintered flux with an alkalinity of about 1.0. It is used in conjunction with low and ultra-low carbon stainless steel welding tapes for arc strip overlay welding of stainless steel transition layers on low carbon and low alloy steels. To prevent excessive chromium burnout, the flux contains a certain amount of chromium to supplement the burnout.

 

Applications：
Arc-banded overlay welding of stainless steel transition layers for chemical vessels, hydrogenation reactor inner walls and pipe plates.

 

Flux chemical composition reference value(%)：

SiO2+TiO2

CaO+MgO

Al203+MnO

CaF2

S

P

25

35

20

20

≤0.03

≤0.04

 

Reference value of chemical composition of cladding metal(%)：

Welding tape

C

Si

Mn

Cr

Ni

S

P

H0Cr24Ni13

≤0.06

≤1.0

≤2.5

18-21

9-11

≤0.03

≤0.03

H00Cr24Ni13

≤0.04

≤1.0

≤2.5

18-21

9-11

≤0.03

≤0.03

 

Notice：

1. The flux shall be baked at 300-350°C for 2 hours before use.

2. Rust, oil, water and other impurities should be removed from the welded parts before welding.
 