WD- SJ101Q Sintering flux for submerged arc welding
WD- SJ101Q Sintering flux for submerged arc welding

Iran WD- SJ101Q Sintering flux for submerged arc welding

WD-SJ101Q is a kind of fluoro-alkali type sintering flux for bridges with alkalinity of about 3.0. It has the appearance of gray spherical particles of 10-60 mesh (2.0-0.28mm).

Category:

Iran· Low Alloy Steel

Phone:400-888-8888

Inquire

Product Description

Standards：

GB/T5293　　S 49 A4 FB-SU34　　AWS A5.17　　F7A4-EH14　　ISO 14174-SAFB 1

 

Introduction：

WD-SJ101Q is a kind of fluoro-alkali type sintering flux for bridges with alkalinity of about 3.0. It has the appearance of gray spherical particles of 10-60 mesh (2.0-0.28mm). The flux in the welding process shows advantages as follows: arc stability; easy deslagging; beautiful weld seam formation; pure deposited metal; has a high low temperature impact toughness. Welding can be used in both AC and DC, DC welding wire connected to the positive electrode.

 

Applications：
The flux is a special flux for welding bridges. It can weld a variety of low-alloy bridge steel and steel for pressure vessels.

 

Flux chemical composition reference value(%)：

SiO2+TiO2

CaO+MgO

Al203+MnO

CaF2

S

P

14.2

33.4

27.8

23.6

0.018

0.020

 

Reference values for mechanical properties of molten metal：

Mating wire

Yield strength
(MPa)

Tensile strength
(MPa)

Elongation
(%)

KV2 (J)

-40°C

H10Mn2

445

550

31.5

122


Notice：

1. The flux shall be baked at 300-350°C for 2 hours before use.

2. Rust, oil, water and other impurities should be removed from the welded parts before welding.
 